BK-887T Rheological Additive
GENERAL INFORMATION
BK-887T is a natural aluminosilicate thickening bentonite agent, the main component is the hydrophilic high-purity special modified montmorillonite, it could replace BentoneLT.
ADVANTAGES
☆ Thixotropy: It is a high thixotropic product. High shear and low viscosity, low shear and high viscosity. It can replace traditional cellulose ether thickening agent.
PHYSICAL PROPERTES |
TYPICAL APPLICATION |
Color/Form:White powder |
Water-based industrial paint |
Fineness through 0.075mm:≥98% |
Water-based anti-corrosion paint |
Moisture(@105℃,2hrs):≤10.0% |
Water-based ink |
2% Aqueous gel viscosity 60r(24h),cp:≥1500 |
Nano-materials |
PH value(2%suspension ):7.0-8.5 |
|
INCORPORATION
BK-887T can be added to the water at the beginning of the dispersion, and it should be added before other components. Dispersing at high speed shear for 10-20minutes. It can also be made into 1% to 2% pregel and then added to the system in the form of pregel. If the pregel is made at low shear, it should be allowed to stand for 12 hours to prevent post-thickening.